Both grade 316 and 316L steels offer high creep strength, stress-to-rupture and tensile strength at high temperatures, as well as excellent corrosion resistance and strength properties. 316/316L Stainless Steel - Penn StainlessPenn Stainless inventory includes 316/316L (UNS S31600 / S31603), in sheet, sheet coil, plate, plate coil, bar, structural and tubular products. Generally, this grade is dual-certified to meet both 316 and 316L. Alloy 316/316L is ideally suited for applications requiring corrosion resistance superior to Type 304 and has good elevated temperature strength.
316/316L STAINLESS STEEL TYPE 316 is widely used in applications requiring corrosion resistance superior to Type 304, or good elevated temperature strength. Typical uses include exhaust manifolds, furnace parts, heat exchangers, jet engine parts, pharmaceutical and photographic equipment, valve and pump trim, chemical equipment, 316L Pipe Sizing Calculations and Tables316L seamless pipe (A312). The physical dimensions and mechanical properties are listed below:Material:316L Size:¾ 2-1/2 Schedule 40 - 160 Wall Thickness:See Chart below O.D. See Chart below Tensile Strength:70,000 psi (ASTM A312) Yield Strength:25,000 psi (ASTM A312) 316L Stainless Steel UNS S31603 Manufacturer UlbrichPropertiesof 316L Stainless Strip in Tempered Conditions. 1/16 Hard. Ultimate Tensile Strength:85 KSI min (585 MPA min) Yield Strength:(0.2% Offset) 45 KSI min (310 MPA min) Elongation:35% Min. 1/8 Hard. Ultimate Tensile Strength:100 KSI min (690 MPA min) Yield Strength
In ASTM A240, type 316 and 316L is a chromium nickel austenitic steel, Element molybdenum addition can enhances corrosion resistance of stainless steel, which is the main factor that 316/316l is more corrosion resistant than 304/304l. When 316L steel of low carbon content is only a little higher than 316 steel on strength level. Stainless Steel - Austenitic - 1.4404 (316L) Bar and Section316 has good resistance to oxidation in intermittent service to 870°C and in continuous service to 925°C. However, continuous use at 425-860°C is not recommended if corrosion resistance in water is required. In this instance 316L is recommended due to its resistance to carbide precipitation. Stainless Steel 316L Bolts and Nuts S31603 Hex Bolt These SS 316L Hex Bolts are a chromium nickel alloy with molybdenum in it. The addition of molybdenum makes the 316L Stainless Steel Stud Bolts Yield Strength to be higher with better anticorrosive properties. There is a lower carbon version of the same material as well.
Mar 02, 2020 · Type 316 steel is an austenitic chromium-nickel stainless steel that contains between two and 3% molybdenum. The molybdenum content increases corrosion resistance, improves resistance to pitting in chloride ion solutions, and increases strength at high temperatures. Type 316 grade stainless steel is particularly effective in acidic environments.Specification Sheet:Alloy 316/316L - Sandmeyer Steelstrength at elevated temperatures. It is common practice for 316L to be dual certified as 316 and 316L. The low carbon chemistry of 316L combined with an addition of nitrogen enables 316L to meet the mechanical properties of 316. Alloy 316/316L resists atmospheric corrosion, as well as, moderately oxidizing and reducing environments.